We often discuss the importance and function of ferrite beads. Since this article was written, we've publish Everything You Need To Know About Ferrite Beads by industry expert Kella Knack.
Sometimes I wish I could see electromagnetic waves. It would make detecting EMI much easier. Instead of having to mess around with complicated setups and signal analyzers, I could just look and see what all the fuss is about. While you may not be able to see EMI, you can sometimes hear it when it comes through audio circuits. One possible fix for that kind of interference is a ferrite bead.
Unfortunately, ferrite beads (also called a ferrite choke, ferrite clamp, ferrite collar, EMI filter bead, or even a ferrite ring filter) can be a bit of a mystery. The ferrite core function resembles that of an inductor, but the ferrite frequency response deviates from this functionality at high frequencies. In order to use them properly, you’ll need to understand their electromagnetic characteristics and how they change during use. After you’ve got a handle on the theory behind ferrite bead uses, you’ll need to carefully select one for your circuit board. If you don’t you could end up causing more problems than you fix.
What is a Ferrite Bead and How Do Ferrite Beads Work?
Ferrite beads are passive electronic components that can suppress high frequency signals on a power supply line. They are normally placed around a power/ground line pair that is incoming to a particular device, such as the power cord for your laptop. These beads work according to Faraday’s Law; the magnetic core around a conductor induces a back EMF in the presence of a high frequency signal, essentially attenuating the ferrite frequency response.
Ferrites are magnetic materials, and placing this material in a ferrite clamp around the power supply/ground line allows provides a source of inductive impedance for signals passing through the line. That might tempt you to think of them as a standard inductor, but they’re more complex than that. In reality, a ferrite bead is a nonlinear component; the impedance it provides changes was the load current and voltage drop across the ferrite change. The simplified circuit model of a ferrite bead will help you understand its frequency characteristics. However, these attributes can change as a function of current and temperature.
Load current can change the impedance of your ferrite.
What are Ferrite Beads Used For?
Because ferrite bead impedance is inductive, ferrite beads are used to attenuate high-frequency signals in electronic components. As a ferrite bead choke can be placed on the power line connecting to an electronic device, it can remove any spurious high frequency noise present on a power connection, or that is output from a DC power supply. This ferrite clamp use is one of many ways to suppress power supply noise, such as that from a switched-mode power supply. This ferrite bead application as a ferrite filter provides suppression and elimination of conducted EMI.
Among the various ferrite bead uses as a filter, an EMI filter bead/power supply filter bead is usually rated for a certain DC current. Currents greater than the specified value can damage the component. The troublesome thing is that this limit is drastically affected by heat. As temperature increases the rated current quickly decreases. Rated current also affects the ferrite's impedance. As DC current increases, a ferrite bead will "saturate" and lose inductance. At relatively high currents, saturation can reduce the ferrite bead impedance by up to 90%.
Ferrite Bead vs. Inductor
Although a ferrite bead can be modeled as an inductor, it does not behave as a typical inductor. If you’re wondering how to measure the behavior of a ferrite bead vs. inductor behavior, you would send an analog signal through the bead and sweep the frequency across several orders of magnitude. If you create a Bode plot for the frequency-swept measurements for a ferrite bead, you’ll find that the ferrite bead provides steeper roll-off at higher frequencies compared to an inductor with similar low frequency behavior.
A ferrite bead can be modeled as capacitors and inductors, and a resistor in parallel, with this RLC network wired with a series resistor. The series resistor quantifies the device’s resistance to DC currents. The inductor in this model represents a ferrite beads primary function of attenuating high-frequency signals, i.e., providing inductive impedance through Faraday’s Law. The parallel resistor in this model accounts for losses in eddy currents that are induced within the ferrite bead at high frequencies. Finally, the capacitor in this model accounts for the component’s natural parasitic capacitance.
When looking at a ferrite bead impedance curve, you can see that the impedance, which is primarily resistive, is extremely high in only a thin band. The inductance of the bead dominates within this thin band. At higher frequencies, the ferrite bead impedance begins to appear capacitive over and the impedance rapidly decreases. Eventually, as frequency continues increasing, the capacitive impedance will drop to a very small value, and the ferrite bead impedance appears purely resistive.
The ferrite core in a ferrite bead provides a similar function as the ferrite core in a transformer.
Ferrite Bead Selection Guide
Now that you’ve got the ferrite theory under your belt, it’s time to choose one for your device. This is not very difficult, and if you want to know how to select a ferrite bead for a design, you just have to pay attention to a bead’s specifications. You may be wondering, are ferrite beads necessary for my design? Like many engineering decisions, the answer is not so simple. If you know that your board will experience conducted EMI within a specific frequency range, and you need to attenuate these frequencies, then a ferrite bead may be the right choice for your design.
Based on the inductive behavior of ferrite beads, it is natural to conclude that ferrite beads “attenuate high frequencies” without much further consideration. However, ferrite beads do not act like a wideband low-pass filter as they can only help attenuate a specific range of frequencies. You must choose a ferrite bead selection and choke where your undesired frequencies are in its resistive band. If you go a little too low or a little too high the bead will not have the desired effect.
Before selecting a specific ferrite bead for your design, you should see if the manufacturer can provide you with impedance vs. load current curves for the ferrite bead. By far, this is the best tool you can use if you are unsure of how to select a ferrite bead. If your load currents are very high, you’ll need to select a ferrite bead that can withstand them without saturating and losing their impedance within the desired frequency range.
Ferrite beads and ferrite chokes are essentially resistive loads at high frequencies, which means they can cause a few problems in your circuit. When placing a bead you’ll need to think about voltage drop and heat dissipation.
In the days of higher voltage circuits, voltage drop wasn’t a big deal. Now we have lots of low power circuits that can use voltages down around 2 V. At those levels, you can’t afford to lose much. Ferrite beads necessarily cause a DC voltage drop in your circuit. It may not seem like much, but if your integrated circuits (ICs) have a short high-current draw state, the loss could become significant. Place your ferrite beads where they won’t cause voltage drop issues.
Since ferrite materials are resistive at high frequencies, they primarily dissipate the absorbed energy as heat. This heat isn’t necessarily a problem for your PCB when a ferrite choke is used on a power supply line, but it can become one when it is used to dissipate high frequencies at high current. If your system is especially noisy and the bead will be absorbing lots of high frequencies this heat could become more of an issue. Make sure to take the bead’s heat dissipation into account.
Ferrite bead impedance will change with temperature.
Ferrite beads can be quite useful, but only if you understand exactly how they work. Remember that they attenuate signals in a fairly small band, and their effectiveness depends on temperature and load current. In order to best use a ferrite bead, you should make sure it meets your exact specifications. Then, when placing the bead, be sure to take voltage drop and heat into account.
Dealing with things like ferrite beads can be difficult, but designing your doesn’t have to be. Altium Designer® is state of the art PCB design software with tools that can help you build the optimal . It even has add-ons like the power delivery network , which can help you deal with problems like voltage drop and heat dissipation.
Have more questions about ferrite beads? Call an expert at Altium.
Check out Altium in action...
Powerful PCB Design
About the AuthorVisit Website More Content by Altium Designer